Impact loading performance of polymer foam core aluminium sandwich panels

No Thumbnail Available

Date

2019-04-01

Authors

Güçlü, H.
Kaşar, I.
Yazıcı, M.

Authors

Can, Yücel
Türkoğlu, I. K.

Journal Title

Journal ISSN

Volume Title

Publisher

Polish Acad Sciences Inst Physics

Research Projects

Organizational Units

Journal Issue

Abstract

In this study, two different foam core aluminum face sheets sandwich panels were developed. The core materials were selected as expanded polypropylene (EPP) and extruded polystyrene (XPS) foams. Two aluminum face sheets and foam cores were combined with flexible epoxy-based adhesives, under 20 N static compression load. The average density of the produced sandwich panels was 0.39 g/cm(3) for EPP foam core sandwich and 0.33 g/cm(3) for XPS foam core sandwich panel. Produced specimens were subjected 3-point bending experiments under impact loading. Damage behavior of the sandwiches was observed using post-mortem pictures. The results show that the produced sandwiches damaged perfectly plastic deformations with face sheets and core. There was not any adhesive and cohesive failure in the core and face sheets interfaces.

Description

Bu çalışma, 24-30 Nisan 2018 tarihleri arasında Fethiye[Türkiye]’da düzenlenen 8. International Advances in Applied Physics and Materials Science Congress and Exhibition (APMAS)’da bildiri olarak sunulmuştur.

Keywords

Aluminum sandwich panel, Epp foam, Xps foam, Impact loading, Adhesive bonding, Science & technology, Physical sciences, Physics, multidisciplinary, Physics

Citation

Collections

0

Views

0

Downloads

Search on Google Scholar