Effect of temperature and rolling direction on the formability of cp2 and ti-6al-4v titanium materials

No Thumbnail Available

Date

2023-09-13

Authors

Gökmen, Şaban
Ertan, Rukiye
Özgül, Hande Güler

Authors

Journal Title

Journal ISSN

Volume Title

Publisher

Walter De Gruyter Gmbh

Research Projects

Organizational Units

Journal Issue

Abstract

Pure (CP2) and alloyed titanium (Ti-6Al-4V) have an important place in biomedical and aerospace applications due to their low density and high strength properties. In this study, the effect of the formability of CP2 and Ti-6Al-4V titanium alloy at different temperatures on mechanical properties and microstructure was investigated. The hot forming process was carried out by pressing 1 mm sheet titanium plates at different temperatures on the U profile mold. Specimens along the rolling direction and perpendicular to the rolling direction were taken from the bottom the formed U-plates. Afterward, tensile tests, microhardness measurements, and changes in microstructure were examined, respectively. As a result, at high temperatures and in different rolling directions, significant changes in microstructure and mechanical properties were observed. It was determined that the best forming temperature of CP2 and Ti-6Al-4V materials along the rolling direction was 500 degrees C, white it is 400 degrees for perpendicular to the rolling direction was 400 degrees C.

Description

Keywords

Microstructure, Cp2, Ti-6al-4v, Hot forming, Mechanical properties, Microstructure, Science & technology, Technology, Materials science, characterization & testing, Materials science

Citation

Collections

0

Views

0

Downloads

Search on Google Scholar